05Х12Н6Д2МФСГТ |
Feот 73.9%Cr11.5-13%Ni5.5-6.5%Cu1.4-2.2%Si0.6-1.2%Ti0.4-0.8%Mn0.2-1.2%V0.2-0.5%Mo0.2-0.4%C0.01-0.08% |
ГОСТ 5950 - 2000 |
11Х4В2МФ3С2 |
Feот 85.6%Cr3.5-4.2%V2.3-2.8%W2-2.7%Si1.4-1.8%C1.05-1.1%Mo0.3-0.5%Mn0.2-0.5% |
ГОСТ 5950 - 2000 |
11ХФ |
Feот 96%C1.05-1.1%Cr0.4-0.7%Mn0.4-0.7%V0.15-0.3%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
12Х1 |
Feот 94.8%Cr1.3-1.65%C1.15-1.2%Mn0.3-0.6%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
13Х |
Feот 95.8%C1.25-1.4%Cr0.4-0.7%Mn0.15-0.4%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
3Х2МНФ |
Feот 93.2%Cr2-2.5%Ni1.2-1.6%Mo0.4-0.6%Mn0.3-0.6%C0.27-0.3%V0.25-0.4%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
4ХМНФС |
Feот 93.4%Cr1.25-1.5%Ni1.2-1.6%Si0.7-1%Mo0.65-0.8%V0.35-0.5%C0.35-0.4%Mn0.15-0.4% |
ГОСТ 5950 - 2000 |
4ХС |
Feот 94.7%Cr1.3-1.6%Si1.2-1.6%C0.35-0.4%Mn0.15-0.4% |
ГОСТ 5950 - 2000 |
5ХВ2СФ |
Feот 93.4%W1.8-2.3%Cr0.9-1.2%Si0.8-1.1%C0.45-0.5%Mn0.15-0.4%V0.15-0.3% |
ГОСТ 5950 - 2000 |
5ХНВ |
Feот 93.5%Ni1.4-1.8%Cr0.8-0.8%Mn0.5-1.8%C0.5-0.6%W0.4-0.7%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
5ХНВС |
Feот 94%Cr1.3-1.6%Ni0.8-1.2%Si0.6-0.9%C0.5-0.6%W0.4-0.7%Mn0.3-0.6% |
ГОСТ 5950 - 2000 |
6Х3МФС |
Feот 93%Cr2.6-3.3%C0.55-0.6%Si0.35-0.6%V0.3-0.6%Mn0.2-0.6%Mo0.2-0.5% |
ГОСТ 5950 - 2000 |
6Х4М2ФС |
Feот 89.8%Cr3.8-4.4%Mo2-2.4%Si0.7-1%C0.57-0.6%V0.4-0.6%Mn0.15-0.4% |
ГОСТ 5950 - 2000 |
6Х6В3МФС |
Feот 85.9%Cr5.5-6.5%W2.5-3.2%Mo0.6-0.9%Si0.6-0.9%V0.5-0.8%C0.5-0.6%Mn0.15-0.4% |
ГОСТ 5950 - 2000 |
7ХФ |
Feот 97.3%C0.63-0.7%Cr0.4-0.7%Mn0.3-0.6%Si0.15-0.3%V0.15-0.3% |
ГОСТ 5950 - 73, в последней версии материал отсутствует |
8Х4В2МФС2 |
Feот 85.9%Cr4.5-5.1%W1.8-2.3%Si1.7-2%V1.1-1.4%Mo0.8-1.1%C0.8-0.9%Mn0.2-0.5% |
ГОСТ 5950 - 2000 |
8Х6НФТ |
Feот 90%Cr5-6%Ni0.9-1.3%C0.8-0.9%V0.3-0.5%Mn0.15-0.4%Si0.1-0.4%Ti0.05-0.1% |
ГОСТ 5950 - 2000 |
8ХФ |
Feот 96.9%C0.7-0.8%Cr0.4-0.7%Mn0.15-0.4%V0.15-0.3%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
9Г2Ф |
Feот 95.4%Mn1.7-2.2%C0.85-0.9%Si0.1-0.4%V0.1-0.3% |
ГОСТ 5950 - 2000 |
9Х1 |
Feот 95.2%Cr1.4-1.7%C0.8-0.95%Si0.25-0.4%Mn0.15-0.4% |
ГОСТ 5950 - 2000 |
9Х5ВФ |
Feот 90.4%Cr4.5-5.5%C0.85-1%W0.8-1.2%Mn0.15-0.4%V0.15-0.3%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
9ХВГ |
Feот 95.1%Mn0.9-1.2%C0.85-0.9%Cr0.5-0.8%W0.5-0.8%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
9ХС |
Feот 94.4%Si1.2-1.6%Cr0.95-1.2%C0.85-0.9%Mn0.3-0.6% |
ГОСТ 5950 - 2000 |
9ХФ |
Feот 96.3%C0.8-0.9%Cr0.4-0.7%Mn0.3-0.6%V0.15-0.3%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
9ХФМ |
Feот 96.1%C0.8-0.9%Cr0.4-0.7%Mn0.3-0.6%W0.15-0.3%Mo0.15-0.2%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
В2Ф |
Feот 95.2%W1.6-2%C1.05-1.2%Cr0.2-0.4%Mn0.15-0.4%V0.15-0.3%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
Х |
Feот 95.1%Cr1.3-1.65%C0.95-1.1%Mn0.15-0.4%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
ХВ4 |
Feот 91.9%W3.5-4.3%C1.25-1.4%Cr0.4-0.7%Si0.15-0.3%V0.15-0.3%Mn0.015-0.4% |
ТУ 5950 - 73 - 73, в последней версии материал отсутствует |
ХВ4Ф |
Feот 91.4%W3.5-4.3%C1.25-1.4%Cr0.4-0.7%Mn0.15-0.4%Si0.15-0.3%V0.115-0.3% |
ГОСТ 5950 - 73, в последней версии материал отсутствует |
ХВГ |
Feот 93.9%W1.2-1.6%Cr0.9-1.2%C0.9-1.05%Mn0.8-1.1%Si0.1-0.4% |
ГОСТ 5950 - 2000 |
ХВСГ |
Feот 94.5%C0.95-1%Si0.65-1%Cr0.6-1.1%Mn0.6-0.9%W0.5-0.8%V0.05-0.1% |
ГОСТ 5950 - 73, в последней версии материал отсутствует |
ХВСГФ |
Feот 94.3%C0.95-1%Si0.65-1%Cr0.6-1.1%Mn0.6-0.9%W0.5-0.8%V0.05-0.1% |
ГОСТ 5950 - 2000 |
ХГС |
Feот 94.1%Cr1.3-1.65%C0.95-1%Mn0.85-1.2%Si0.4-0.7% |
ГОСТ 5950 - 2000 |